    题名: 鈣矽基彈性骨水泥
    Elastic Calcium Silicate Matrix Bone Cement
    作者: 王偉仲
    Wei-Chung Wang
    贡献者: 中山醫學大學:口腔醫學院;口腔材料科學研究所;丁信智
    关键词: 骨水泥;生物活性;徑向拉伸強度;硬化時間;溶膠凝膠法
    Bone cement;Bioactivity;Diametral tensile strength;Setting time;Bone repair
    日期: 2008-07-29
    上传时间: 2010-11-05T07:19:51Z (UTC)
    摘要: 本研究開發一具有快速硬化、生物活性之骨填補材料。藉由溶膠凝膠法合成出的鈣矽粉體，經過研磨後再與液體溶液混合形成骨水泥，除了分析粉體性質外，骨水泥浸泡於模擬體液前後之性質將為研究焦點。結果顯示溶膠凝膠法合成出的鈣矽粉體經研磨後顆粒大小約1μm，與液體混合後硬化時間最快在10 分鐘之內。骨水泥徑向拉伸最大強度為2.73 MPa。而在體外測試方面，將試片浸泡於人體模擬體液中，發現隨著時間的增加，磷灰石層形成越為明顯，並且不會造成強度衰減。而將幾丁聚醣和明膠加入骨水泥中也發現經過浸泡後會有磷灰石層的產生。因此我們認為本材料擁有良好的生物活性，並可預期成為一骨填補材料。
    The aim of this study was to synthesize bone cement with fast-setting and bioactivity for bone substitute applications. The sol-gel derived calcium/silicon powders were ground, followed by mixing with liquid phase. The study focuses on characterization of the bone cement before and after immersion in physiologically simulated solution, in addition to evaluation of properties of as-prepared powders. The results indicated that the particles size of ground was about 1μm. When mixing with the liquid phase, the setting time of the cement from powder was within 10 min. The diametral tensile strength value of the bone cement neither increase with increase in calcium content nor decrease with decrease in silicon content. The highest strength value is about 2.73 MPa. Regarding in vitro testing in simulated body fluid (SBF), the formation of apatite layer was apparent with increasing immersion time. And, the immersion time did not degrade the strength of the bone cement. The addition of naturally chitosan and gelatin to ceramic cements were also induce the precipitated apatite layer. Last not the least, the presently developed cements had a good bioactivity, which are expected as a potential bone repair material.
    URI: https://ir.csmu.edu.tw:8080/handle/310902500/2567
    显示于类别:[口腔科學研究所] 博碩士論文

    文件中的档案:

    档案 描述 大小格式浏览次数
    index.html0KbHTML280检视/开启


    SFX Query

    在CSMUIR中所有的数据项都受到原著作权保护.

    TAIR相关文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈