In vitro and in vivo osteogenesis of gelatin-modified calcium silicate cement with washout resistance

doi:10.1016/j.msec.2020.111297

中山醫學大學機構典藏 CSMUIR > 中山醫學大學研究成果 > 期刊論文 > Item 310902500/24479

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://ir.csmu.edu.tw:8080/ir/handle/310902500/24479

题名:	In vitro and in vivo osteogenesis of gelatin-modified calcium silicate cement with washout resistance
作者:	Wu, IT;Kao, PF;Huang, YR;Ding, SJ
关键词:	Bone cement;Calcium silicate;Calcium sulfate;Gelatin;Bone repair
日期:	2020
上传时间:	2022-08-09T08:03:01Z (UTC)
出版者:	ELSEVIER
ISSN:	0928-4931
摘要:	The purpose of this study was to evaluate the physicochemical properties and the in vitro and in vivo osteo- genesis of the newly developed calcium silicate containing 5 wt% gelatin (CSG) cement compared with calcium silicate (CS) and calcium sulfate hemihydrate (CSH) cements. In addition to the phase composition and microstructure, washout resistance, setting time, and diametral tensile strength of the bone cements were also performed. In vitro examination of cell growth, differentiation, and mineralization were performed with macrophage cell line (RAW 264.7), MG63 human osteoblast-like cells, and human mesenchymal stem cells (hMSCs). The mini-pig model with mandibular alveolar bone defect was used to assess the in vivo function of cement. Histological and histomorphometric assessments were performed at 6 and 12 weeks after implantation. The results indicated that the CS and CSG powders were mainly composed of poorly crystalline beta-dicalcium silicate, and the irregular CSH powders had a highly crystalline phase. After setting, the product of CS and CSG was calcium-silicate-hydrate gel and CSH exhibited a plate-like gypsum crystal structure. The setting time of CS, CSG, and CSH was 19, 35, and 10 min, respectively. Gelatin effectively improved the washout resistance and diametral tensile strength of CS from 2.4 MPa to 3.4 MPa, while CSH had no washout resistance and its strength was 7.6 MPa. The osteogenic activity of MG63 and hMSC cells on the CSG cement surface was consistently shown to be significantly higher than that on the CSH cement surface. Interestingly, CS and CSG cements exhibited lower macrophage expression compared to CSH cements. Twelve week after implantation, the amount of new bone in the defect area of the CS group was slightly higher than that of the CSG and CSH groups. It is concluded that CSG cement had improved anti-washout performance, favorable osteogenesis in vitro and in vivo, which was beneficial for clinical application.
URI:	http://dx.doi.org/10.1016/j.msec.2020.111297 https://www.webofscience.com/wos/woscc/full-record/WOS:000573293900009 https://ir.csmu.edu.tw:8080/handle/310902500/24479
關聯:	MATERIALS SCIENCE & ENGINEERING C-MATERIALS FOR BIOLOGICAL APPLICATIONS ,2020 ,v117
显示于类别:	[中山醫學大學研究成果] 期刊論文

文件中的档案:

档案	描述	大小	格式	浏览次数
index.html		0Kb	HTML	267	检视/开启

在CSMUIR中所有的数据项都受到原著作权保护.

TAIR相关文章

数据加载中.....