Osteoporosis and its related problems such as fractures are gradually becoming common due to an aging population. Current methods to treat osteoporosis include medical and surgical options such as bone implants. Recent developments in 3D printing and materials science technologies has allowed us to fabricate individualized scaffolds with desired properties. In this study, we mixed Xu Duan into strontium-calcium silicate powder at 5% (XD5) and 10% (XD10) and fabricated 3D scaffolds with polycaprolactone. All scaffolds were assessed for its physical, mechanical, and biological properties to evaluated for its feasibility for bone tissue engineering in the osteoporosis model. Our results showed that such a scaffold could be fabricated using extrusion-based printing techniques and that addition of XD did not alter original structural properties of the SrCS. Furthermore, the XD5 and XD10 scaffolds were found to be non-toxic to cells and cells cultured on the scaffolds had significantly higher proliferation and secreted increased osteogenic-related proteins in in vitro studies as compared to the XD0 groups. Remarkably, the XD10 scaffolds could be used as substitutes for the critical-sized bone defect (7.0 mm diameter and 8.0 mm depth) in the osteoporotic rabbit model. The XD10 scaffolds can enhance bone ingrowth and accelerate new bone regeneration even in complex osteoporotic pathological environments. These results showed that such a Chinese medicine-contained scaffold had potential in osteoporosis bone tissue regeneration and could be considered as a promising tool for future clinical used applications.