Calcium silicate layer on titanium fabricated by electrospray deposition

doi:10.1016/j.msec.2019.01.011

中山醫學大學機構典藏 CSMUIR > 口腔醫學院 > 口腔醫學研究所 > 期刊論文 > Item 310902500/19906

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://ir.csmu.edu.tw:8080/ir/handle/310902500/19906

题名:	Calcium silicate layer on titanium fabricated by electrospray deposition
作者:	Ding, S.-J.
日期:	2019-03
上传时间:	2019-03-15T03:18:21Z (UTC)
ISSN:	09284931
摘要:	Titanium and its alloys have been used as implant materials. Non-ideal osseointegration of the implant materials has facilitated the development of the bioactive coatings on the implant surfaces. In this work, the bioactive calcium silicate (CaSi) powder prepared in a green synthesis route was used to cover the surface of Ti implants by a facile electrospray deposition method. Post annealing in air was also applied to form the oxidation layer on the Ti surface with the aim of increasing the bond strength between the CaSi coating layer and Ti substrate. For the characterization of the coatings several analytical methods such as X-ray diffraction, scanning electron microscopy, secondary neutral mass spectrometry, and Raman-spectroscopy were used, in addition to the measurement of bond strength and corrosion resistance. The results indicated a uniform CaSi layer with a thickness of about 1 μm deposited on the Ti substrate. Annealing in the range of 700–900 °C in air resulted in the formation of rutile phase of TiO 2 ; more importantly, annealing at 800 °C did not significantly affect the composition of the CaSi layer consisting of β-Ca 2 SiO 4 . The bond strength between the coating layer and Ti substrate can be remarkably enhanced at an annealing temperature of 700 or 800 °C compared with the as-prepared coating without annealing. The annealed coatings had a better corrosion resistance than the as-prepared coating. It is concluded that the electrospray method associated with the post-annealing can be successfully used for the deposition of a CaSi layer with a defined structure and composition on titanium implants. © 2019 Elsevier B.V.
URI:	https://ir.csmu.edu.tw:8080/ir/handle/310902500/19906
關聯:	Materials Science and Engineering C Volume 98, May 2019, Pages 401-408
显示于类别:	[口腔醫學研究所] 期刊論文

文件中的档案:

档案	描述	大小	格式	浏览次数
Calcium-silicate-layer-on-titanium-fabricated-by-electrospray-deposition2019Materials-Science-and-Engineering-C.pdf		1378Kb	Adobe PDF	186	检视/开启

检视Licence

在CSMUIR中所有的数据项都受到原著作权保护.

TAIR相关文章

数据加载中.....