Conversion of CuS thin films to structured nanosheet CuyS (1 &lt; y 蠆 2) by vacuum annealing

中山醫學大學機構典藏 CSMUIR > 口腔醫學院 > 牙醫學系暨碩士班 > 期刊論文 > Item 310902500/18250

jsp.display-item.identifier=請使用永久網址來引用或連結此文件: https://ir.csmu.edu.tw:8080/ir/handle/310902500/18250

题名:	Conversion of CuS thin films to structured nanosheet CuyS (1 <;y 蠆 2) by vacuum annealing
作者:	Shi, J.B.;Wu, P.F.;Chen, Y.C.;Chang, Y.C.;Tsai, M.Z.;Cheng, F.C.;Kao, C.T.;Lee, H.W.;Chen, M.Y.;Huang, Y.J.;Huang, R.Y.;Lin, S.K.
关键词:	CuyS;Electrodeposition;Nanosheet thin films;Optical properties
日期:	2014
上传时间:	2017-08-09T04:43:19Z (UTC)
出版者:	Wiley-VCH Verlag
ISSN:	2321300
摘要:	In this study, large-area and uniform thickness novel nanosheet structured CuS thin films on ITO glass have been prepared by the one-step electrodeposition method from a dimethyl sulfoxide solution. Thin films of completely preserved nano-sheet like morphology of CuyS (y = 1.75, 1.8, 1.95, and 2.0) are grown by vacuum annealing CuS thin films at 500°C for different lengths of time. The 500°C sample heated for 10 hours was nearly converted to single phase of Cu2S with y ∼ 2. The optical direct band gaps of nano-sheet CuyS thin films annealed at 500°C of 2, 6, and 10 hours in vacuum were found to be 1.94, 1.68, and 1.44 eV, respectively. © 2014 Wiley-VCH Verlag GmbH & Co. KGaA.
URI:	http://dx.doi.org/10.1002/crat.201400176 https://www.scopus.com/inward/record.uri?eid=2-s2.0-84912124742&doi=10.1002%2fcrat.201400176&partnerID=40&md5=99fcac023f0fe8c222115bfc90386dbc https://ir.csmu.edu.tw:8080/ir/handle/310902500/18250
關聯:	Crystal Research and Technology 49(11) ,860-864