    题名: Synthesis and optical properties of single-crystalline indium zinc oxide (IZO) nanowires via co-deposition and oxidation methods
    作者: Shi, J.-B.;Wu, P.-F.;Lin, Y.-T.;Kao, C.-T.;Chen, Chen C.-J.;Cheng, F.-C.;Liu, H.-H.;Chen, Y.-C.;Lin, H.-S.;Lee, H.-W.
    关键词: AAM;Indium zinc oxide;Nanowire
    日期: 2015
    上传时间: 2017-08-09T04:42:34Z (UTC)
    出版者: Elsevier Ltd
    ISSN: 0042207X
    摘要: In this study, one-dimensional (1D) indium zinc oxide (IZO; Indium oxide with heavy zinc doping of 30 at %) nanowires was synthesized via electrodeposition and an oxidization method with porous anodic alumina membrane (AAM), which had an average diameter of about 60 nm. As FE-SEM results showed the synthesized IZO nanowires had an approximate length of 6-8 μm with a high aspect ratio of about 116. IZO nanowires with an Zn/(In + Zn) atomic ratio of 0.301 (∼0.3) were observed from EDS. XRD and SAED analyses show the synthesized nanowires were of single-crystal cubic structure. The UV/Visible/NIR absorption of the IZO nanowires showed an absorption peak of around 330 nm with a direct band gap energy (Eg) of 3.5 eV. © 2015 Elsevier Ltd. All rights reserved.
    URI: http://dx.doi.org/10.1016/j.vacuum.2015.02.005
    https://www.scopus.com/inward/record.uri?eid=2-s2.0-84923783788&doi=10.1016%2fj.vacuum.2015.02.005&partnerID=40&md5=49e3591cd1511d0bb7ff0b137cbd0cf5
    https://ir.csmu.edu.tw:8080/ir/handle/310902500/18233
    關聯: Vacuum 115 ,61-65