Poly(dopamine) coating of 3D printed poly(lactic acid) scaffolds for bone tissue engineering

doi:10.1016/j.msec.2015.06.028

中山醫學大學機構典藏 CSMUIR > 口腔醫學院 > 牙醫學系暨碩士班 > 期刊論文 > Item 310902500/18224

請使用永久網址來引用或連結此文件: https://ir.csmu.edu.tw:8080/ir/handle/310902500/18224

題名:	Poly(dopamine) coating of 3D printed poly(lactic acid) scaffolds for bone tissue engineering
作者:	Kao, C.-T.;Lin, C.-C.;Chen, Y.-W.;Yeh, C.-H.;Fang, H.-Y.;Shie, M.-Y.
關鍵詞:	3D printed-scaffold;Angiogenic;Dopamine;Osteogenic;Poly(lactic acid);Tissue engineering
日期:	2015
上傳時間:	2017-08-09T04:42:11Z (UTC)
出版者:	Elsevier Ltd
ISSN:	9284931
摘要:	3D printing is a versatile technique to generate large quantities of a wide variety of shapes and sizes of polymer. The aim of this study is to develop functionalized 3D printed poly(lactic acid) (PLA) scaffolds and use a mussel-inspired surface coating to regulate cell adhesion, proliferation and differentiation of human adipose-derived stem cells (hADSCs). We prepared PLA 3D scaffolds coated with polydopamine (PDA). The chemical composition and surface properties of PDA/PLA were characterized by XPS. PDA/PLA modulated hADSCs' responses in several ways. Firstly, adhesion and proliferation, and cell cycle of hADSCs cultured on PDA/PLA were significantly enhanced relative to those on PLA. In addition, the collagen I secreted from cells was increased and promoted cell attachment and cell cycle progression were depended on the PDA content. In osteogenesis assay, the ALP activity and osteocalcin of hADSCs cultured on PDA/PLA were significantly higher than seen in those cultured on pure PLA scaffolds. Moreover, hADSCs cultured on PDA/PLA showed up-regulation of the ang-1 and vWF proteins associated with angiogenic differentiation. Our results demonstrate that the bio-inspired coating synthetic PLA polymer can be used as a simple technique to render the surfaces of synthetic scaffolds active, thus enabling them to direct the specific responses of hADSCs. © 2015 Elsevier B.V. All rights reserved.
URI:	http://dx.doi.org/10.1016/j.msec.2015.06.028 https://www.scopus.com/inward/record.uri?eid=2-s2.0-84935008792&doi=10.1016%2fj.msec.2015.06.028&partnerID=40&md5=cf4fec8b2e2eed6558ab4ef150c42013 https://ir.csmu.edu.tw:8080/ir/handle/310902500/18224
關聯:	Materials Science and Engineering C 56 ,165-173
顯示於類別:	[牙醫學系暨碩士班] 期刊論文