    題名: Impact Behavior of Three Notched All-Ceramic Restorations after Soaking in Artificial Saliva
    作者: Yan, Min;Wei, Chung-Kai;Lin, Yuh-Yih;Hu, Suh-Woan;Ding, Shinn-Jyh
    貢獻者: 中山醫大口腔科學研究所
    關鍵詞: all-ceramic restorations;impact energy;leucite-reinforced ceramic;lithium disilicate ceramic;zirconia;saliva
    日期: 2015-07-20
    上傳時間: 2016-08-05T04:18:27Z (UTC)
    ISSN: 1996-1944
    摘要: Biomechanics play a critical role in influencing the clinical applications of all-ceramic dental restorations. The restorative biomaterials have to demonstrate mechanical durability in the oral environment because they are always exposed to a variety of oral environments. This study was designed to evaluate the effect of soaking time, notch and saliva pH values on the impact energy of three commonly used all-ceramic materials for CAD/CAM. The leucite-reinforced glass ceramic (ProCAD), lithium disilicate glass ceramic (IPS e.max CAD) and zirconia-based ceramic materials (IPS e.max ZirCAD) were used. The experimental results indicated that the impact energy of ProCAD decreased with an increase in soaking time, but not for IPS e.max CAD and IPS e.max ZirCAD. The impact energy of the zirconia system was higher than leucite-reinforced and lithium disilicate-based ceramic systems. When subjected to preformed 0.5 mm U-shape notch on the bar specimen of 3 mm thick, the impact energy of the all-ceramic restorations revealed a markedly reduction of about 80%–90%, almost irrespective of dental compositions, which indicated the effect of flaw to a great degree. No statistically significant influence (p > 0.05) of pH values (4, 7 and 9) on impact energy was found for each group. It is concluded that the no matter which all-ceramic materials were used, it was appreciably sensitive to the presence of notches. The ceramic composition and microstructure have been shown to affect mechanical durability.
    URI: https://ir.csmu.edu.tw:8080/ir/handle/310902500/15646
    http://dx.doi.org/10.3390/ma8074479
    關聯: Materials 2015, 8(7), 4479-4490
    顯示於類別:[口腔醫學研究所] 期刊論文

    文件中的檔案:

    檔案 描述 大小格式瀏覽次數
    index.html0KbHTML421檢視/開啟


    檢視Licence

    SFX Query

    在CSMUIR中所有的資料項目都受到原著作權保護.

    TAIR相關文章

    DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回饋